Synthesis and Characterization of Eu(III)-Incorporated Silica Nanoparticles for a Red LED
2013년 8월 29일 17시 19분 16초
이곳을 클릭하시면 발표코드에 대한 설명을 보실 수 있습니다.
10월 16일 (수요일) 16:00~19:00
충남대학교 화학과, Korea
The powdered complex and the complex-incorporated silica particles were fabricated with 365-nm UV-LEDs. The PL properties of the fabricated LEDs operated at 3.0 V were investigated as a function of time. Figure 5 shows the intensity decay of the red emission. The intensity of the red emission from the powder-casted LED was decreased rapidly by 80 % as soon as the LED was on. The powdered complex was significantly degraded by the heat emitted from the pumping UV-LED, of which the junction temperature was higher than 150 ?C. Contrary, for the CS and the IS complexes, the intensity was maintained without loss after slightly down at the initial stage, while for the OS complex the intensity was gradually decreased. These results indicated that the silica matrix capping the complex well protected the complex from the thermal degradation. Figure 6a shows PL spectra of the fabricated LED devices. The PL spectra consisted of two strong bands. The sharp band and its satellite, peaking at 360 nm and 410 nm, respectively, were due to an emission from the pumping InGaN diode, and the low-energy bands, appearing in the 590 ? 700 nm region, were due to the emission from Eu(III). The relative intensity between the two strong bands was dependent on an amount of the casted phosphor. The CIE 1931 chromaticity of the three devices is shown in Figure 6b. The chromaticity index (x, y) varied from (0.5467, 3382) for the IS-fabricated LED and (0.5505, 0.3342) for the CS-fabricated LED to (0.4682, 0.3437) for the OS-fabricated LED. This blue-shift of the x-index was dependent on the relative intensity of the 410-nm satellite band to that of the red emission.
등록된 그림이 있는경우 그림을 클릭하시면 원본 그림파일을 볼 수 있습니다.
최종본을 확인하지 않아 발생된 문제에 대해서는 책임지지 않습니다.
미리보기의 그림위치는 임시 위치입니다. 모든 그림파일은 Abstract 하단에 위치하게 됩니다.